Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F13%3A%230000771" target="_blank" >RIV/26722445:_____/13:#0000771 - isvavai.cz</a>
Alternative codes found
RIV/00216305:26210/14:PU105785
Result on the web
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.569" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.569</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.569" target="_blank" >10.4028/www.scientific.net/KEM.592-593.569</a>
Alternative languages
Result language
angličtina
Original language name
Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking
Original language description
This paper deals with fracture of neutron irradiated austenitic Ti-stabilized stainiess steel 08Ch18N1 OT. The steel had been tested in air and in water environment (320°C) using several kind of tests representing different stress strain conditions for crack initiation and growth. Especially two tests, Slow Strain Rate and Crack Growth Rate, applied in water. Without irradiation the steel did not suffer stress corrosion cracking in the water, but on irradiated specimens appeared areas of intergranular fracture mixed with transgranular cleavage-like facets and secondary cracks. IASCC phenomenon manifested for the intergranular fracture appearance. The differences between fracture of irradiated and non-irradiated specimens in air and in water are documented and discussed.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JF - Nuclear energy
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/ED2.1.00%2F03.0108" target="_blank" >ED2.1.00/03.0108: Sustainable Energy</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Key Engineering Materials
ISSN
1662-9795
e-ISSN
—
Volume of the periodical
592-293
Issue of the periodical within the volume
November
Country of publishing house
CH - SWITZERLAND
Number of pages
4
Pages from-to
569-572
UT code for WoS article
—
EID of the result in the Scopus database
—