Microscopic Evaluation of Protective Coating by Coated Sheet safter Corrosion Load

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F12%3A43884448" target="_blank" >RIV/44555601:13420/12:43884448 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Microscopic Evaluation of Protective Coating by Coated Sheet safter Corrosion Load

Original language description

Introduction into problems - The aim of the paper was microscopically analyze protective layer by coated sheets after corrosion loading which were pre-treated by various ways. The samples were divided into 4 groups according to the pretreatment type andduration of corrosion load. After a corrosive effect on the corrosion chamber the protective layer was subjected to microscopic evaluation. For samples of group I and IV have to degrade the protective layer and the formation of corrosion products on thebase material which causes degradation of the protective layer and shorten its life. For samples of group II and III microstructural analysis showed good condition of the painted surface layer and the base material showed no presence of corrosion products. It again confirms the need for compliance of technological conditions for the pretreatment of the surface particularly in the application of modern less aggressive means.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JK - Corrosion and material surfaces

OECD FORD branch

—

Project

—

Continuities

S - Specificky vyzkum na vysokych skolach

Publication year

2012

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Volume of the periodical

12

Issue of the periodical within the volume

13

Country of publishing house

CZ - CZECH REPUBLIC

Number of pages

7

Pages from-to

151-157

UT code for WoS article

—

EID of the result in the Scopus database

—