Influence of Ca, Sb and heat treatment on AlSi9CuMnNi alloy in frame of their structure

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F19%3A43895254" target="_blank" >RIV/44555601:13420/19:43895254 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1007/978-3-319-91334-6_79" target="_blank" >http://dx.doi.org/10.1007/978-3-319-91334-6_79</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/978-3-319-91334-6_79" target="_blank" >10.1007/978-3-319-91334-6_79</a>

Result language
angličtina
Original language name
Influence of Ca, Sb and heat treatment on AlSi9CuMnNi alloy in frame of their structure
Original language description
Treatment of metal alloys is one of the ways to affect the quality and properties of the material at the Faculty of Mechanical Engineering of the Jan Evangelista Purkyně University in Ústí nad Labem, one part of the research consists of searching for the influence of various modifying and inoculating elements on selected aluminum alloys. One of the alloys undergoing the present research is the hardening aluminum alloy AlSi9CuMnNi. The article describes one from these experiments. AlSi9CuMnNi alloy was modified with various amounts of calcium (0.05, 0.1 and 0.15 wt% Ca) and 0.2 wt% Sb. The alloy without modification and with 0.2 wt% Sb was heat-treated, too. In the experiment were made three castings for each type of alloy. The final structure of each casting was analyzed.
Czech name
—
Czech description
—

Project
<a href="/en/project/ED4.1.00%2F11.0260" target="_blank" >ED4.1.00/11.0260: Education improvement & research expansion at FPTM</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)