Properties od Polyaniline/montmorillonite thin Films in dependenceon preparation temperature

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13440%2F15%3A43886695" target="_blank" >RIV/44555601:13440/15:43886695 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Properties od Polyaniline/montmorillonite thin Films in dependenceon preparation temperature
Original language description
A simple method was used for the preparation of polyaniline/montmorillonite (PANI/MMT) nanocomposite thin films deposited on glass slides. Water solution of anilinium sulfate (as a precursor) was mixed with the ammonium peroxydisulfate (as an oxidizing agent) in presence of glass slide and an appropriate amount of MMT at different temperatures. Two following temperatures were used: 10 degrees C and 20 degrees C. Layered structure of the MMT significantly affects the ordering of PANI chains, i.e. the PANI nanostructure. PANI/MMT thin films contain no other components like additional polymeric carriers or binders. Present work is focused on how the change of temperature of preparation mixture affect the thickness, morphology and electrical conductivity of resulting PANI/MMT nanocomposite films. Raman spectroscopy, atomic force microscopy and conductivity measurement were used for the characterization of the samples.
Czech name
—
Czech description
—

Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)