The synthesis of Au-NPs by ion implantation in the crystalline GaN and characterisation of their optical properties

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13440%2F22%3A43897448" target="_blank" >RIV/44555601:13440/22:43897448 - isvavai.cz</a>

  • Result on the web

    <a href="https://www.epj-conferences.org/articles/epjconf/abs/2022/05/epjconf_anpc2022_01003/epjconf_anpc2022_01003.html" target="_blank" >https://www.epj-conferences.org/articles/epjconf/abs/2022/05/epjconf_anpc2022_01003/epjconf_anpc2022_01003.html</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1051/epjconf/202226101003" target="_blank" >10.1051/epjconf/202226101003</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    The synthesis of Au-NPs by ion implantation in the crystalline GaN and characterisation of their optical properties

  • Original language description

    Nanostructured surfaces with embedded noble metal nanoparticles is an attractive way for manipulation with the optical properties of wide bandgap semiconductors applied in optoelectronics, photocatalytic processes or for Surface-Enhanced Raman spectroscopy. Ion implantation offers an effective way for nanoparticle preparation without the use of additional chemicals that offers precise control of nanoparticle depth distribution. The aim of this study is a synthesis of the gold nanoparticles in GaN by implantation of 1.85 MeV Au ions with high fluences up to 7x1016 cm-2 and study of optical properties of Au implanted GaN. Implanted crystals were annealed at 800 oC in an ammonia atmosphere for 20 min to support Au nanoparticle creation and GaN recovery. The structure characterisation has been realized by Rutherford backscattering spectroscopy in channelling mode and it showed the formation of two separated disordered regions ? the surface region and buried layer. The lower implantation fluences induce damage mainly in a buried layer; however, the increase of the Au-ion fluence leads to the increase of surface disorder as well. Further, the increase of the Au-ion fluence induces the Au dopant shift to the surface and multimodal Au-depth profiles. TEM analyses confirmed the formation of Au nanoparticles in the implanted samples after annealing with sizes up to 14 nm. The increase of light absorption and modification of GaN bandgap of the Au modified GaN was deduced from the change in optical transmission spectra between 370 ? 1400 nm.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>ost</sub> - Miscellaneous article in a specialist periodical

  • CEP classification

  • OECD FORD branch

    10301 - Atomic, molecular and chemical physics (physics of atoms and molecules including collision, interaction with radiation, magnetic resonances, Mössbauer effect)

Result continuities

  • Project

  • Continuities

    S - Specificky vyzkum na vysokych skolach

Others

  • Publication year

    2022

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    EPJ Web of Conferences

  • ISSN

    2100-014X

  • e-ISSN

    2100-014X

  • Volume of the periodical

    2022

  • Issue of the periodical within the volume

    261

  • Country of publishing house

    FR - FRANCE

  • Number of pages

    8

  • Pages from-to

    1-8

  • UT code for WoS article

  • EID of the result in the Scopus database