Failure behaviour of cladding made from Sv 07Kh25N13 austenitic stainless steel
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46356088%3A_____%2F21%3AN0000030" target="_blank" >RIV/46356088:_____/21:N0000030 - isvavai.cz</a>
Alternative codes found
RIV/61388998:_____/21:00536631 RIV/68407700:21340/21:00353380
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S0308016120302507" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0308016120302507</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.ijpvp.2020.104275" target="_blank" >10.1016/j.ijpvp.2020.104275</a>
Alternative languages
Result language
angličtina
Original language name
Failure behaviour of cladding made from Sv 07Kh25N13 austenitic stainless steel
Original language description
Sv 07Kh25N13 is austenitic stainless steel used in nuclear industry. Due to its excellent corrosion resistance in the environment of WWER type nuclear reactor primary circuit, it is applied as anticorrosive cladding of the reactor pressure vessel. In this paper, results of detailed experimental research of failure behaviour of the cladding are presented. Static fracture toughness values J(0.2) exhibited an extreme scatter. Metallographic analysis performed on the fractured specimens revealed large variations of structure within every single cladding layer. Fracto-graphic analysis performed on fracture surfaces revealed considerable variations of micromechanisms taking place during ductile crack propagation. Conclusions on the relationship between the local microstructure, the failure mode and the fracture toughness of the cladding were drawn. Results indicate that the fracture toughness of the cladding was primarily determined by local amount of sigma phase in the area of crack propagation.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20305 - Nuclear related engineering; (nuclear physics to be 1.3);
Result continuities
Project
<a href="/en/project/EF15_003%2F0000493" target="_blank" >EF15_003/0000493: Centre of Excellence for Nonlinear Dynamic Behaviour of Advanced Materials in Engineering</a><br>
Continuities
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Others
Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
International Journal of Pressure Vessels and Piping
ISSN
0308-0161
e-ISSN
—
Volume of the periodical
189
Issue of the periodical within the volume
February
Country of publishing house
GB - UNITED KINGDOM
Number of pages
7
Pages from-to
1-7
UT code for WoS article
000614145400017
EID of the result in the Scopus database
2-s2.0-85097455003