Dimensional changes of the castings from Zn alloys in the process of solidification monitoring

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F06%3A%400000225" target="_blank" >RIV/46747885:24210/06:@0000225 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Dimensional changes of the castings from Zn alloys in the process of solidification monitoring
Original language description
The article deals with measure of the dimensional changes of the castings from Zn and Al alloys during their solidification. There was built up a measuring apparatus for this purpose. This apparatus is consists of a converter from an analog signal for adigital signal (Polish provenience), a PC and a chase whereon it is a mould with the measuring detector of the dilatation. The mould has shape of roll with a cave for cast of the castings ? 60 x 70 mm. The dilatation curves the both alloys were obtainedthese castings by the solidification. In the case of Al-alloys it was observed an influence of chemical composition and metallurgical treatment (use of refining salts) on linear changes during solidification and on the dimension of the shrinkage originating
Czech name
Sledování rozměrových změn odlitků ze slitin Zn během tuhnutí
Czech description
Článek se zabývá měřením lineárních změn odlitků ze slitin Zn a Al v průběhu jejich tuhnutí. Pro tento účel bylo sestaveno měřící zařízení, které aplikuje dilatometr polské provenience. Při odlévání odlitků ? 60 x 70 mm byly získány dilatační křivky obou slitin. U slitin hliníku byl sledován vliv chemického složení a metalurgického ošetření (použití rafinačních solí) na lineární změny.