Effect of curing time and curing temperature on mechanical properties of carbon fiber based geopolymer

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F13%3A%230005706" target="_blank" >RIV/46747885:24210/13:#0005706 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Effect of curing time and curing temperature on mechanical properties of carbon fiber based geopolymer
Original language description
Geopolymers are still considered as a new material for coatings and adhesives, a new binder for fiber reinforced composites, and a new cement for concrete. Fiber-reinforced composites based on geopolymer matrix (geocomposite) have been well-known for over 20 years, since the first Davidovits? patent was filed. These new materials can be fabricated and cured at room temperature or thermoset in a simple autoclave. After approximately several hours of curing, these materials exhibit excellent features suchas lightweight and high strength but are also ideally fire resistant, with nontoxic fumes and smokes, and resist all organic solvents. After 28 days, the image of scanning microscope, compressive strength of geopolymer adding C-fiber with 1%, 3 %, 5 %,7 %, 8 %, 10 % in weight were observed in different curing time at 2000C, 3000C, 6000C, 8000C.
Czech name
—
Czech description
—

Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
MMK 2013: Mezinárodní Masarykova konference pro doktorandy a mladé vědecké pracovníky
ISBN
978-80-87952-00-9
ISSN
—
e-ISSN
—
Number of pages
9
Pages from-to
10
Publisher name
Magnanimitas
Place of publication
Hradec Králové
Event location
Hradec Králové
Event date
Jan 1, 2013
Type of event by nationality
CST - Celostátní akce
UT code for WoS article
—

Similar results(10)