The Influence of Heat-Treatment on the Phase Composition and Coefficient of Thermal Expansion of Fe3Al-Type Alloy with Niobium Addition
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F15%3A00001963" target="_blank" >RIV/46747885:24210/15:00001963 - isvavai.cz</a>
Alternative codes found
RIV/46747885:24620/15:00001963
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
The Influence of Heat-Treatment on the Phase Composition and Coefficient of Thermal Expansion of Fe3Al-Type Alloy with Niobium Addition
Original language description
Iron aluminides belong to a group of intermetallic materials. Atoms of intermetallics are long-distance arranged that's why these alloys show some interesting properties as high temperature strength or corrosion resistance. Besides of beneficial properties iron aluminides have some disadvantages as e.g. brittleness at room temperature or a sharp drop in strength above 600 °C. It has been shown that the high temperature mechanical properties can be enhanced through third element addition. The structure of Fe3Al alloy with addition of niobium was studied in two states - as cast state and in state after stabilization annealing at 1000 °C for 50 hours. Phase composition was investigated for these samples, because it can affect the alloy properties. The phase composition was determined using scanning electron microscopy (SEM) equipped by energy dispersive analysis (EDX) and electron backscattered diffraction detector (EBSD). The influence of heat-treatment on coefficient of thermal expansion (CTE) was also studied. The CTE's were measured by means of horizontal dilatometer.
Czech name
—
Czech description
—
Classification
Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20501 - Materials engineering
Result continuities
Project
<a href="/en/project/GAP108%2F12%2F1452" target="_blank" >GAP108/12/1452: Optimizing the high temperature mechanical properties of iron aluminides of Fe3Al type with carbide forming elements</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Volume of the periodical
15
Issue of the periodical within the volume
4
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
6
Pages from-to
705-710
UT code for WoS article
—
EID of the result in the Scopus database
2-s2.0-84949221336