Fractal geometry used for evaluation of corrosion resistance of Fe-14Al-6Cr wt.% against molten glass

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F15%3A00002462" target="_blank" >RIV/46747885:24210/15:00002462 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Fractal geometry used for evaluation of corrosion resistance of Fe-14Al-6Cr wt.% against molten glass
Original language description
Corrosive attack of metals and alloys by molten glass can be described by parameters of surface roughness. Fractal geometry and statistic tools were used for surface roughness quantification. The obtained parameters of fractal geometry and statistics were determined on boundary curves between alloys and glass which had been generated from the digital photography of sample cross-section. This methodology was successfully used for quantification of surface changes of iron aluminides Fe-14Al-6Cr and austenitic steel during corrosion test in molten soda-lime glass at 1200°C.
Czech name
—
Czech description
—

Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20506 - Coating and films

Project
<a href="/en/project/GAP108%2F12%2F1452" target="_blank" >GAP108/12/1452: Optimizing the high temperature mechanical properties of iron aluminides of Fe3Al type with carbide forming elements</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)