The influence of CH4/N2 Gas ratio on the structure and chemical composition of Cr(C, N) coatings deposited by CAD technology

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F18%3A00006072" target="_blank" >RIV/46747885:24210/18:00006072 - isvavai.cz</a>
Result on the web
<a href="http://Energy" target="_blank" >http://Energy</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.21062/ujep/201.2018/a/1213-2489/MT/18/6/917" target="_blank" >10.21062/ujep/201.2018/a/1213-2489/MT/18/6/917</a>

Result language
angličtina
Original language name
The influence of CH4/N2 Gas ratio on the structure and chemical composition of Cr(C, N) coatings deposited by CAD technology
Original language description
This article presents the study of the influence of the bias voltage and CH4/N2 gas ratio on the structure and chemical composition of Cr(C,N) coatings. The coatings were deposited by cathodic arc evaporation of pure Cr (99.99 %) cathode under an atmosphere of a mixture of CH4 and N2 gasses at the low deposition temperature of 300 °C. The ratio of reactive gasses was changed from 0 to 100 %. Energy-dispersive spectroscopy showed a linear dependence of resulting C/N ratio on the process gas ratio. The roughness of layers prepared from a mixture of process gasses is higher compared to pure gasses.
Czech name
—
Czech description
—

Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20506 - Coating and films

Project
<a href="/en/project/EG15_019%2F0004853" target="_blank" >EG15_019/0004853: Dynamic multi-axis electro-hydraulic recovery units</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2018
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)