EMI Shielding Effectiveness of Polypyrrole Coated Glass Fabric

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F13%3A%230001602" target="_blank" >RIV/46747885:24410/13:#0001602 - isvavai.cz</a>
Result on the web
<a href="http://www.davidpublishing.com/show.html?12072" target="_blank" >http://www.davidpublishing.com/show.html?12072</a>
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
EMI Shielding Effectiveness of Polypyrrole Coated Glass Fabric
Original language description
Polypyrrole was coated on E-glass fibre fabric by vapor deposition technique using FeCl3 as oxidizing agent and TsO- (tosylate) as dopant. The very low resistive (below 500 ohm. sq) samples were specially prepared by multiple dips. EMI shielding effectiveness was measured at 800 MHz 1.8 GHz and 2.4 GHz, which varies according to frequency and found to be increased with increase in electrical conductivity of the samples. IL (Insertion loss) of highly conductive glass fabric sample was calculated and shows that 99.23% of the EM incident radiations can be blocked with the help of this technique.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JJ - Other materials
OECD FORD branch
—

Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)