Needleless Electrospinning of Silk fibroin/Polycaprolactone Blend Nanofibres

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F15%3A00003523" target="_blank" >RIV/46747885:24410/15:00003523 - isvavai.cz</a>
Alternative codes found
RIV/46747885:24620/15:00003523
Result on the web
<a href="http://www.nanocon.eu/files/uploads/01/NANOCON%202014%20content.pdf" target="_blank" >http://www.nanocon.eu/files/uploads/01/NANOCON%202014%20content.pdf</a>
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Needleless Electrospinning of Silk fibroin/Polycaprolactone Blend Nanofibres
Original language description
In this study, composite electrospun fibres consisting of silk fibroin and polycaprolactone was fabricated by needleless electrospinning method. The electrospinning of silk fibroin/ polycaprolactone blends with different composition ratios was performedwith formic acid as a spinning solvent. The effects of blend ratio of silk fibroin/polycaprolactone in spinning solution is investigated as a function of the properties of spinning solution, the morphology of electrospun fibres and the spinning performance of electrospinning process. Result sho wed that an increase in the weight ratio of polycaprolactone in spinning solution produces a significant effect on the fibre diameter of the electrospun fibre and the spinning performance of process. With an increase in the amount of polycaprolactone in sp inning solution decreasing the fibre diameter and the spinning performance of electrospining process. The silk fibroin/ polycaprolactone blend fibres had diameters ranging from 200 to 1100 nm.