Self-cleaning and stiffness characteristics of TiO2-cellulose coated cotton fabric
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F16%3A00003862" target="_blank" >RIV/46747885:24410/16:00003862 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Self-cleaning and stiffness characteristics of TiO2-cellulose coated cotton fabric
Original language description
In this report, a new method to make cotton fabric self-cleaning and permanently stiff by coating cellulose-TiO2on its surface is demonstrated. Nano TiO2 was dispersed in cellulose solution (cellulose in 60% H2SO4 solution) in order to coat it on cotton fabric. The surface morphology of cellulose-TiO2nanoparticles coated sample was analyzed by SEM. Characteristic peak of TiO2 in X-ray diffraction pattern at 24.2° and appearance of white particles on the surface of the cotton fabric in SEM micrographs confirmed the successful coating process. The Orange II dye was used as stain and its degradation was observed under UV light. X-ray diffraction analysis showed that cellulose II content increases slightly (by 5.3%) after the solvent treatment. Washing fastness study showed that the fabric stiffness was permanent and self-cleaning properties were stable up to 10 multiple washings. Air and water vapor permeability was not decreased considerably, whereas tensile strength was increased significantly after coating
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JJ - Other materials
OECD FORD branch
—
Result continuities
Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů