Thermal Analysis of PEG/Metal Particle-coated Viscose Fabric

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24410%2F21%3A00008898" target="_blank" >RIV/46747885:24410/21:00008898 - isvavai.cz</a>

Alternative codes found

RIV/46747885:24620/21:00008898

Result on the web

<a href="https://www.sciencedirect.com/science/article/pii/S0142941821001811" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0142941821001811</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.polymertesting.2021.107231" target="_blank" >10.1016/j.polymertesting.2021.107231</a>

Result language

angličtina

Original language name

Thermal Analysis of PEG/Metal Particle-coated Viscose Fabric

Original language description

The introduction of metal particles (MP) in the phase change materials (PCM) realizes the highly efficient thermal energy storage. However, a suitable carrier is necessary for PCM/MP composites for various applications. In this work, the polyethylene glycol (PEG) was used as PCM, five MPs including copper (Cu), aluminum (Al), silver (Ag), iron (Fe), and zinc (Zn) particles were used, and the viscose fabric was selected as a carrier for coating of PEG/MPs. The PEG was blended with different MPs with the same weight ratio of 72.3:23.7. Then, the PEG/MP-coated viscose fabric was prepared by applying PEG/MP composites on the viscose fabric with the same weight ratio of 90:10 and the PEG-coated viscose fabric (86.7:13.3) was set as reference. The phase transition of the prepared PEG/MP composites and the PEG/MP-coated viscose fabrics was investigated via the differential scanning calorimetry (DSC). The thermal behavior of the PEG/MP-coated viscose fabric was investigated via Alambeta device and the T-history method. The results revealed that the enthalpy of all the PEG/MP-coated viscose fabrics were larger than 100J/g. Besides, only the higher theoretical enthalpy of the PEG in the PEG/MP composites was found, and the MPs assisted in the higher crystallization of PEG. Results from the Alambeta device proved that the thermal conductivity was increased when MPs were introduced in the coated viscose fabric. T-history curves of all the PEG/MP-coated viscose fabric revealed that the heating constant of the phase transition stage mainly accounted for the quick heat transfer.

Czech name

—

Czech description

—

Type

J_imp - Article in a specialist periodical, which is included in the Web of Science database

CEP classification

—

OECD FORD branch

20500 - Materials engineering

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Publication year

2021

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

POLYMER TESTING

ISSN

0142-9418

e-ISSN

—

Volume of the periodical

100

Issue of the periodical within the volume

AUG

Country of publishing house

GB - UNITED KINGDOM

Number of pages

14

Pages from-to

—

UT code for WoS article

000677592700036

EID of the result in the Scopus database

2-s2.0-85111052931