Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24510%2F21%3A00009321" target="_blank" >RIV/46747885:24510/21:00009321 - isvavai.cz</a>
Alternative codes found
RIV/00216305:26620/21:PU139447
Result on the web
<a href="https://doi.org/10.1016/j.jeurceramsoc.2020.11.029" target="_blank" >https://doi.org/10.1016/j.jeurceramsoc.2020.11.029</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2020.11.029" target="_blank" >10.1016/j.jeurceramsoc.2020.11.029</a>

Result language
angličtina
Original language name
Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics
Original language description
This work shows for the first time the possibility to sinter BCZT powder compacts by rapid heating rates within one hour of sintering, while achieving good piezoelectric properties. The sintering was performed by rapid (heating rates 100 and 200 degrees C/min) pressure-less sintering (PLS) at 1550 degrees C/5-60 min and by SPS sintering (100 degrees C/min, 1450 degrees C/5 60 min and 1500 degrees C/15 45 min). The rapid PLS samples reached a relative density up to 94 % and grain sizes of 17-36 mu m acquiring d(33) up to 414 pC/N. Although the SPS samples reached full density at 1450 degrees C, their piezoelectric properties worsened due to smaller grains (10-15 mu m) as well as formation of cracks at dwell times ` 30 min. At elevated SPS temperature of 1500 degrees C/30 min, the d(33) increased to 360 pC/N sustaining full density. Even higher increase in d(33) (424 pC/N) of SPS samples was achieved by post-rapid PLS at 1550 degrees C/60 min resulting from further expansion in grain size.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20504 - Ceramics

Project
<a href="/en/project/GA18-20498S" target="_blank" >GA18-20498S: Control of microstructure and properties of lead-free piezoceramic materials through advanced ceramic processing</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)