Analysis of Cracked Rail of the Crane of Type A120

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F21%3AN0000051" target="_blank" >RIV/47718684:_____/21:N0000051 - isvavai.cz</a>
Result on the web
<a href="https://www.vzuplzen.cz/" target="_blank" >https://www.vzuplzen.cz/</a>
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Analysis of Cracked Rail of the Crane of Type A120
Original language description
The aim of the work was to find out the causes of cracking of the A120 crane track rail. Although the track was regularly inspected by defectoscopic techniques, after five years of operation, the rail was broken at the weldment. The elemental composition of the welded joint materials was verified and the mechanical properties were determined. A fractographic description of the fracture surface was performed and the structure of the material was evaluated. Several factors contributed to the formation of crack, the combination of which led to a rail failure. Defects of the welded joint, acting as notches, from which they initiated fatigue cracks, unfavourable microstructure of the weld metal, low toughness of the base material and operating environment and conditions were dominant.
Czech name
—
Czech description
—

Project
<a href="/en/project/TN01000007" target="_blank" >TN01000007: National Centre for Energy</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Přínos metalografie pro řešení výrobních problémů
ISBN
978-80-01-06883-0
ISSN
—
e-ISSN
—
Number of pages
8
Pages from-to
257-254
Publisher name
České vysoké učení technické v Praze
Place of publication
Praha
Event location
Mariánské Lázně
Event date
Sep 21, 2021
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)