Miniaturization in Thixoforming

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F10%3A00503749" target="_blank" >RIV/49777513:23210/10:00503749 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Miniaturization in Thixoforming
Original language description
Innovative technological processes can help us to obtain unconventional structures with specific mechanical properties, even from conventional materials. Forming metal alloys in the semi-solid state is one of many ways. With thixoforming the tool steel X210Cr12 was treated with rapid solidification from the liquid phase. The microstructure after processing in the semi-solid state is 96% globular austenite formations surrounded by a carbide network. The aim of the experiment was to test the new technological process and to describe the obtained microstructure and its stability. The stability of the microstructure was tested under various thermal constraints and mechanical loading. The hardness of the austenite component after thixoforming was about 320HV 0.05; hardness of the carbide network was about 550 HV 0.05.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JQ - Machinery and tools
OECD FORD branch
—

Project
<a href="/en/project/1M06032" target="_blank" >1M06032: RESEARCH CENTRE OF FORMING TECHNOLOGY</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)