Evaluation of in-situ deformation experiments of TRIP steel

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F17%3A43931580" target="_blank" >RIV/49777513:23210/17:43931580 - isvavai.cz</a>

  • Result on the web

    <a href="http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012059/pdf" target="_blank" >http://iopscience.iop.org/article/10.1088/1757-899X/179/1/012059/pdf</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1088/1757-899X/179/1/012059" target="_blank" >10.1088/1757-899X/179/1/012059</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Evaluation of in-situ deformation experiments of TRIP steel

  • Original language description

    The paper reports on the behaviour of low alloyed TRIP (transformation induced plasticity) steel with Niobium during tensile test. The structures were analysed using in-situ tensile testing coupled with electron backscattering diffraction (EBSD) analysis carried out in scanning electron microscope (SEM). Steel specimens were of same chemical composition; however three different annealing temperatures, 800 °C, 850 °C and 950 °C, were applied to the material during the heat treatment. The treatment consisted of annealing for 20 minutes in the furnace; cooling in salt bath after the heating and holding at 425 °C for 20 minutes for all the samples. Untreated bar was used as reference material. Flat samples for deformation stage were cut out of the heat-treated bars. In situ documentation of microstructure and crystallography development were carried out during the deformation experiments. High deformation lead to significant degradation of EBSD signal.

  • Czech name

  • Czech description

Classification

  • Type

    D - Article in proceedings

  • CEP classification

  • OECD FORD branch

    20501 - Materials engineering

Result continuities

  • Project

    <a href="/en/project/LO1502" target="_blank" >LO1502: Development of Regional Technological Institute</a><br>

  • Continuities

    P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Others

  • Publication year

    2017

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Article name in the collection

    IOP Conference Series-Materials Science and Engineering

  • ISBN

  • ISSN

    1757-8981

  • e-ISSN

    neuvedeno

  • Number of pages

    7

  • Pages from-to

    1-7

  • Publisher name

    IOP PUBLISHING LTD

  • Place of publication

    Bristol

  • Event location

    Pilsen

  • Event date

    Nov 9, 2016

  • Type of event by nationality

    WRD - Celosvětová akce

  • UT code for WoS article

    000403407100059