Analysis of Weld Line Influence on Strength of Nylon Parts
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F17%3A43932375" target="_blank" >RIV/49777513:23210/17:43932375 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Analysis of Weld Line Influence on Strength of Nylon Parts
Original language description
Main aim of this article is description of weld line influence on mechanical properties of plastic parts. Special design of mold was created for this research. This mold is able to create specimens with and without weld lines. These specimens undergone tensile test according standard ASTM D638 with different results. Strength and strain results were compared for both types of specimens. Nylon PA6 without any internal reinforcement was used as reference material during testing. Both specimens were investigated also by microscope in order to see composition of weld line and plastic material. Microstructure showed geometry of weld line and also fracture surfaces indicated presence of plastic deformation
Czech name
—
Czech description
—
Classification
Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20301 - Mechanical engineering
Result continuities
Project
<a href="/en/project/LO1502" target="_blank" >LO1502: Development of Regional Technological Institute</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Volume of the periodical
17
Issue of the periodical within the volume
4
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
4
Pages from-to
561-565
UT code for WoS article
—
EID of the result in the Scopus database
2-s2.0-85029567106