Residual stress and nanohardness gradients in surface layers of polished steel samples

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F06%3A00000253" target="_blank" >RIV/49777513:23520/06:00000253 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Residual stress and nanohardness gradients in surface layers of polished steel samples
Original language description
The aim of the contribution is to present the results of X-ray diffraction analysis of both the macroscopic and microscopic residual stresses in polished surface layers of five different steels. Mechanical properties of as-received materials were obtained by tensile tests. The instrumented nanoindentation testing was applied for surface characterization as well. The main goal of the investigation was to find correlations between the lattice deformation of the studied surfaces, their microhardness and mechanical properties.
Czech name
Zbytkové napětí a gradienty nanotvrdosti v povrchových vrstvách leštěných vzorků
Czech description
Cílem této práce je prezentovat výsledky rentgenové difrakční analýzy makro- a mikroskopických zbytkových napětí v povrchových vrstvách leštěných vzorků. Mechanické vlastnosti byly získány tahovou zkouškou, ke zjištění povrchových vlastností byla použitananoindentace. Hlavním cílem bylo najít korelace mezi deformací mřížky zkoumaných povrchů, jejich mikrotvrdostí a mechanickými vlastnostmi.