Composite material properties degradation induced by the cyclic loading
Original language description
The paper deals with the material properties (stiffness, residual strength) degradation of the composite materials induced by the cyclic loading. Basic mechanism of the long fibre composites failure is described. The approaches of composite fatigue failure assessment are listed. Fatigue tests in repeated tension were performed employing the C/E specimens. The fibre orientation was 0°, 45° and 90°. Stiffness and residual strength of these specimens were recorded during the cyclic loading.
Czech name
Změna mechanických vlastností kompozitního materiálu při cyklickém zatěžování
Czech description
Příspěvek se zabývá změnou mechanických vlastností (tuhost, zbytková pevnost) kompozitních materiálů při cyklickém zatěžování. Jsou uvedeny základní mechanismy porušování dlouhovláknových kompozitních materiálů a přístupy hodnocení jejich únavového poškození. Byly provedeny cyklické zkoušky v míjivém tahu vzorků z materiálu C/E s orientací vláken 0°, 45° a 90°. U těchto vzorků byla zaznamenávána změna tuhosti a zbytkové pevnosti při cyklickém zatěžování.