The Effect of Plasma Nitriding on the Corrosion Resistance of Martensitic Stainless Steel X12Cr13
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F16%3A00532896" target="_blank" >RIV/60162694:G43__/16:00532896 - isvavai.cz</a>
Result on the web
<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
The Effect of Plasma Nitriding on the Corrosion Resistance of Martensitic Stainless Steel X12Cr13
Original language description
The plasma nitriding technology was applied on the martensitic stainless steel X12Cr13. The influence of plasma nitriding on the corrosion resistance of selected material was investigated. The chemical composition of selected steel was verified using the Q4 TASMAN device. The plasma nitriding process was performed using two stage nitriding procedure. After plasma cleaning procedure at 515 °C for 45 min in nitriding atmosphere ratio 20H2:2N2 (l/h) was the first stage nitriding procedure performed at 520°C for 16 hours in nitriding atmosphere ratio 25H2:5N2 (l/h) and followed by second stage of nitriding procedure performed at 525°C for 4 hours in nitriding atmosphere ratio 28H2:4N2 (l/h). The microstructure and mechanical properties of the nitride layers were studied using the OES spectrometry, optical microscopy, and hardness testing. The depths of plasma nitride layers were also estimated using cross-sectional microhardness profiles measuring. The corrosion resistance testing of plasma nitrided stainless steel X12Cr13 samples were carried out in a 5 % neutral sodium chloride solution (NSS) in accordance with ISO 9227 standard in the VLM GmbH SAL 400-FL corrosion chamber and visually evaluated. Microhardness and surface hardness of experimental samples were significantly increased, but the corrosion resistance significantly decreased.
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
JK - Corrosion and material surfaces
OECD FORD branch
—
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
17. Medzinárodná vedecká konferencia Transfer 2016
ISBN
978-80-8075-756-4
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
1-6
Publisher name
FŠT TnUAD v Trenčíne
Place of publication
Trenčín
Event location
Hotel Most Slávy, Trenčianske Teplice
Event date
Oct 11, 2016
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—