The effect of annealing temperature on properties of powder metallurgy processed Ti-35Nb-2Zr -0.5O alloy
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F17%3AN0000011" target="_blank" >RIV/60193247:_____/17:N0000011 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S1751616117303181" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1751616117303181</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jmbbm.2017.07.032" target="_blank" >10.1016/j.jmbbm.2017.07.032</a>
Alternative languages
Result language
angličtina
Original language name
The effect of annealing temperature on properties of powder metallurgy processed Ti-35Nb-2Zr -0.5O alloy
Original language description
Ti-35Nb-2Zr-0.5O (wt%) alloy was prepared via a powder metallurgy process (cold isostatic pressing of blended elemental powders and subsequent sintering) with the primary aim of using it as a material for bio-applications. Sintered specimens were swaged and subsequently the influence of annealing temperature on the mechanical and structural properties was studied. Specimens were annealed at 800, 850, 900, 950, and 1000 °C for 0.5 h and water quenched. Significant changes in microstructure (i.e. precipitate dissolution or grain coarsening) were observed in relation to increasing annealing temperature. In correlation with those changes, the mechanical properties were also studied. The ultimate tensile strength increased from 925 MPa (specimen annealed at 800 °C) to 990 MPa (900 °C). Also the elongation increased from ~ 13% (800 °C) to more than 20% (900, 950, and 1000 °C).
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20501 - Materials engineering
Result continuities
Project
<a href="/en/project/TA02010409" target="_blank" >TA02010409: Surface nanostructuring of titanium materials</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
ISSN
1751-6161
e-ISSN
—
Volume of the periodical
—
Issue of the periodical within the volume
75
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
10
Pages from-to
252-261
UT code for WoS article
000412959000030
EID of the result in the Scopus database
—