Influence of cyclic degradation in saline solution on mechanical properties of adhesive bonds
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41310%2F16%3A70586" target="_blank" >RIV/60460709:41310/16:70586 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Influence of cyclic degradation in saline solution on mechanical properties of adhesive bonds
Original language description
The adhesive bond is the complex of three layers - adhesive bonded material (called adherent), adhesive layer and cohesive layer. Degradation aspects act all parts of the adhesive bond. The aim of this research was the evaluation of influence of degradation environment on the strength of structural two-component epoxy adhesives. Adhesive bonds and process of testing the adhesive bonds were in accordance with standard ČSN EN 1465. The degradation environment in form of 5 % saline solution was used within this experiment. Adhesive bonded testing samples were subjected to cyclic loading of saline solution. On the basis of evaluation of performed experiments it is possible to say, that resulting strength of adhesive bonds decreases at simultaneous acting of environment. The strength of adhesive bond after 8th cycle, i.e. after 56 days, significantly decreased from 67 to 78 %. Using the electron microscopy within the experimental research it was proved that the spontaneous failure of the adhesive layer oc
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JR - Other machinery industry
OECD FORD branch
—
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2016
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Manufacturing Technology
ISSN
1213-2489
e-ISSN
—
Volume of the periodical
16
Issue of the periodical within the volume
1
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
6
Pages from-to
204-209
UT code for WoS article
—
EID of the result in the Scopus database
—