Comparative analysis of compressive strength of epoxy adhesive compounds containing fillers
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60460709%3A41310%2F23%3A100681" target="_blank" >RIV/60460709:41310/23:100681 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1080/00218464.2023.2286295" target="_blank" >https://doi.org/10.1080/00218464.2023.2286295</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1080/00218464.2023.2286295" target="_blank" >10.1080/00218464.2023.2286295</a>
Alternative languages
Result language
angličtina
Original language name
Comparative analysis of compressive strength of epoxy adhesive compounds containing fillers
Original language description
The aim of this paper was to analyse the compressive strength and structure of epoxy adhesive compounds containing three different fillers with good thermal conductivity, additionally prepared in variants containing different amounts of these fillers. The base of epoxy adhesive compounds was a mixture of epoxy resin and polyamide curing agent. Three fillers: aluminium, graphite and copper were used in the study. The content of each filler in the epoxy adhesive compounds was 0.5 g, 1 g and 2 g per 100 g of epoxy resin. It allowed to compare the influence of the fillers on the compressive strength between the tested epoxy adhesive compounds and on the structure of the epoxy compounds based on SEM images. To accurately show the differences between the tested samples the one-way ANOVA test and POST-HOC test were used in the study. Descriptive statistic showed that adding the fillers in the amounts used in this research, increased the compressive strength of the epoxy adhesive compounds with the same filler. The results of this analysis showed that the epoxy adhesive compounds containing the aluminium and the copper do not show statistical significance between the amounts of the used filler.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20401 - Chemical engineering (plants, products)
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2023
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
JOURNAL OF ADHESION
ISSN
0021-8464
e-ISSN
0021-8464
Volume of the periodical
101
Issue of the periodical within the volume
2023-01-01
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
25
Pages from-to
—
UT code for WoS article
001107538200001
EID of the result in the Scopus database
2-s2.0-85178303223