Preparation of Mortar for Restoration of Architectural Monuments

Original language description

Mortar mixtures were prepared considering the microscopic observation, granulometric analysis, mercury porosimetry, XRD analysis, thermogravimetric and differential thermal analysis of the original plaster. Two series of lime mortar samples containing identical mixture of aggregates and admixtures but varying in the kind of a lime binder were prepared. In addition, the sample series varied in the ratio between mixing aggregate and binder. Prepared test bodies were subjected to accelerated carbonation process. Carbonated samples were characterized by the measurement of compressive strength, open porosity, water absorption and resistance to salt crystallization. The samples were also again compared with the original plaster by optical microscopy and XRDanalysis. Based on the results of analyses of the original plasters and prepared samples of repair mortar the sample containing lime slurry with the mixture of aggregates in the mixing ratio of 1 : 2 was recommended for the restoration pr

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

AL - Art, architecture, cultural heritage

OECD FORD branch

—

Project

—

Continuities

S - Specificky vyzkum na vysokych skolach

Publication year

2012

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Ceramics-Silikáty

ISSN

0862-5468

e-ISSN

—

Volume of the periodical

56

Issue of the periodical within the volume

3

Country of publishing house

CZ - CZECH REPUBLIC

Number of pages

11

Pages from-to

"269?279"

UT code for WoS article

—

EID of the result in the Scopus database

—