Effect of T-stress on dislocation emission in iron

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388998%3A_____%2F04%3A00103497" target="_blank" >RIV/61388998:_____/04:00103497 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Effect of T-stress on dislocation emission in iron
Original language description
Continuum predictions for dislocation emission from a crack tip loaded under mode I, biaxial conditions, are compared with atomistic results for bcc iron. The simulations validate the continuum prediction that, as the T-stress increases, so does the threshold for dislocation nucleation; hence, the propensity for brittle response increases.
Czech name
Vliv T-napětí na emisi dislokací v železe
Czech description
Predikce kontinua o emisi dislokací od kořene trhliny, zatíženého v tahovém módu I a biaxiálně, jsou porovnány s atomárními výsledky pro alfa železo. Atomární simulace potvrzují predikci kontinua, že se vzrůstem T-napětí se zvyšuje práh pro nukleaci dislokací a tudíž pravděpodobnost křehkého lomu vzrůstá.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2004
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)