Crack orientation versus ductile-brittle behavior in 3D atomistic

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61388998%3A_____%2F07%3A00305939" target="_blank" >RIV/61388998:_____/07:00305939 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Crack orientation versus ductile-brittle behavior in 3D atomistic
Original language description
The paper presents results of molecular dynamic (MD) simulations in 3D bcc iron crystals with edge pre-existing cracks (001)[110] and (110) [110] (crack plane/crack front) loaded uni-axially in tension mode I at temperature of 300 K. The iron crystals inMD have the same orientation and similar geometry as in our recent fracture tests performed at room temperature on iron (3wt.%Si) single crystals [1].
Czech name
Orientace trhliny a štěpně-tvárné chování v 3D atomárních simulacích
Czech description
Článek prezentuje výsledky simulací metodou molekulární dynamiky (MD) v 3D krystalech ?-Fe s pre-existujícími okrajovými trhlinami (001)[110] a (-110)[110] (rovina trhliny / čelo trhliny) zatíženými v tahovém módu I při teplotě 300K. Krystaly železa v MDmají stejnou orientaci a podobnou geometrii jako v našich lomových experimentech při pokojové teplotě, provedených na monokrystalech Fe-(3hm%)Si.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
<a href="/en/project/GA101%2F07%2F0789" target="_blank" >GA101/07/0789: Nano-scale detection of defects by molecular dynamics in 3D</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)