The Influence of hte Composition of the Weld Metal on the Stress Fields around the Welds on the High-Sttrength Ferritic Steel Weldox 700

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389005%3A_____%2F23%3A00582833" target="_blank" >RIV/61389005:_____/23:00582833 - isvavai.cz</a>

  • Result on the web

  • DOI - Digital Object Identifier

Alternative languages

  • Result language

    angličtina

  • Original language name

    The Influence of hte Composition of the Weld Metal on the Stress Fields around the Welds on the High-Sttrength Ferritic Steel Weldox 700

  • Original language description

    The high-strength steels are developed in order to provide the favorable mechanical properties and higher corrosion resistance in relation to conventional carbon steel grades Weldox 700 is such a general structural steel with a minimum yield strength of 650 - 700 MPa. Typical applications are very demanding e.g. load-bearing, structures, pipes, bridges, steel structures storage tanks etc. which are very often composed of the welded parts. The quality of the welds depends besides other things on the residual stresses in the vicinity of the welds. Therefore, the influence of the weld metal chemical composition on residual stress distribution in the vicinity of test welds was studied. Butt welds were prepared in a high-strength steel using two basic shielded metal arc electrodes ─ one conventional producing a bainitic weld metal and one experimental low temperature transformation (LTT) electrode depositing a martensitic weld metal. Welding was done under restraint in a test frame. Residual stress components were measured across the weld using neutron diffraction after removing the test weld from the frame. It was found that the stresses were generally on a lower level for the LTT weld. The largest difference was seen for the transverse residual stress some distance into the heat affected zone.

  • Czech name

  • Czech description

Classification

  • Type

    D - Article in proceedings

  • CEP classification

  • OECD FORD branch

    10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Result continuities

  • Project

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2023

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Article name in the collection

    Proceedings of the RRFM European Research Reactor Conference 2023

  • ISBN

    978-92-95064-39-3

  • ISSN

  • e-ISSN

  • Number of pages

    9

  • Pages from-to

    11-19

  • Publisher name

    European Nuclear Society

  • Place of publication

    Brussel

  • Event location

    Antwerp

  • Event date

    Apr 16, 2023

  • Type of event by nationality

    EUR - Evropská akce

  • UT code for WoS article