Raman spectra and optical properties of selected Bi2O3-PbO-B2O3-GeO2 glasses
Original language description
Some glasses Bi2O3-PbO-B2O3-GeO2 were prepared. Raman spectra indicate an increase in the density of three body linkages with a decrease in B2O3 content. Optical band gap values were determined in the region3.46 -3.6 eV. Temperature shift of the opticalband gap was found at around 4.43-5.610-4 eV/K. Nonlinear refractive index was estimated at around 8.1510-11 esu.
Czech name
Ramanova spektra a optické vlastnosti vybraných skel Bi2O3-PbO-B2O3-GeO2
Czech description
Některá skla Bi2O3-PbO-B2O3-GeO2 systému byla připravena. Ramanova spektra indikují růst hustoty tříatomových můstků s poklesem koncentrace B2O3. Optická šířka zakázaného pásu (Eg) byla určena v intervalu 3.46 -3.6 eV. Teplotní posun Eg byl nalezen v intervalu 4.43-5.610-4 eV/K. Nelineární index lomu byl odhadnut okolo 8.1510-12 esu.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
CA - Inorganic chemistry
OECD FORD branch
—

Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)