The effect of gamma irradiation in air and inert atmosphere on structure and properties of unfilled or glass fibre-reinforced polyamide 6

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F16%3A00459329" target="_blank" >RIV/61389013:_____/16:00459329 - isvavai.cz</a>

  • Result on the web

    <a href="http://dx.doi.org/10.1007/s00289-015-1576-0" target="_blank" >http://dx.doi.org/10.1007/s00289-015-1576-0</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1007/s00289-015-1576-0" target="_blank" >10.1007/s00289-015-1576-0</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    The effect of gamma irradiation in air and inert atmosphere on structure and properties of unfilled or glass fibre-reinforced polyamide 6

  • Original language description

    Crosslinking of polyamide 6 (PA) and filled one with glass fibres (PA/GF) was initiated via macroradical formation by gamma irradiation either in air or in inert argon atmosphere. The crosslinked portion was found to start at absorbed dose around 300 kGy and achieved about 60 and 40 wt% for PA and PA/GF, respectively, if irradiation proceeded in inert, while in air molecular weight increase was only observed without crosslinked gel formation. DSC indicated that irradiation leads to a decrease in crystallinity as well as lamellae thickness. Besides crosslinking, scission of polymer chains also occurs. Modest increase of impact strength was found for PA while small decrease for PA/GF was observed. The dependence of Young’s modulus values on the irradiation dose indicates a minimum around gel point being more pronounced for PA compared to the composite. Irradiation resulted in minor changes in tensile strength and elongation at break while a substantial increase in the elongation at yield was found for PA if irradiated in inert atmosphere. Generally, the application of an optimal dose of gamma irradiation in air results in an increase of toughness of PA without changing other mechanical properties.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

  • CEP classification

    CD - Macromolecular chemistry

  • OECD FORD branch

Result continuities

  • Project

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2016

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    Polymer Bulletin

  • ISSN

    0170-0839

  • e-ISSN

  • Volume of the periodical

    73

  • Issue of the periodical within the volume

    6

  • Country of publishing house

    DE - GERMANY

  • Number of pages

    20

  • Pages from-to

    1775-1794

  • UT code for WoS article

    000376248900019

  • EID of the result in the Scopus database

    2-s2.0-84948430983