Facile preparation of water-dispersible carboxylated polyaniline
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389013%3A_____%2F23%3A00565694" target="_blank" >RIV/61389013:_____/23:00565694 - isvavai.cz</a>
Result on the web
<a href="https://www.sciencedirect.com/science/article/pii/S0379677922002430?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0379677922002430?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.synthmet.2022.117249" target="_blank" >10.1016/j.synthmet.2022.117249</a>
Alternative languages
Result language
angličtina
Original language name
Facile preparation of water-dispersible carboxylated polyaniline
Original language description
Polyaniline (PANI), containing carboxylic groups, was prepared by covalent modification of PANI base, using various amounts of thiolactic acid (TLA). It was found that using the excess of TLA, compared to the stoichiometric amount required for modification of emeraldine form of PANI, did not lead to increase of substitution degree. Elemental analysis showed that in all studied conditions ≈6.5 wt% of carboxylic groups were introduced into PANI backbone. Change of PANI chemical structure as a result of modification by TLA was studied by electronic, vibrational and photoelectron spectroscopy. It was shown that TLA is covalently bound to PANI without significant amount of free TLA and the initial PANI base also becomes partially protonated. Conductivity of PANI-TLA materials (≈5 ×10–7 S cm–1) increased by 4 orders of magnitude, compared to PANI base (5 ×10–11 S cm–1). Due to the presence of carboxylic groups, TLA-modified PANI is dispersible in alkaline aqueous medium, which can enable eco-friendly ways of PANI deposition for the applications in sensors and anticorrosive coatings.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
10404 - Polymer science
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2023
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Synthetic Metals
ISSN
0379-6779
e-ISSN
0379-6779
Volume of the periodical
293
Issue of the periodical within the volume
March
Country of publishing house
CH - SWITZERLAND
Number of pages
7
Pages from-to
117249
UT code for WoS article
000989480500001
EID of the result in the Scopus database
2-s2.0-85144340865