In-situ observation of crack propagation in thermally sprayed coatings
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F10%3A00350810" target="_blank" >RIV/61389021:_____/10:00350810 - isvavai.cz</a>
Alternative codes found
RIV/68407700:21340/10:00173266
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
In-situ observation of crack propagation in thermally sprayed coatings
Original language description
In-situ observation of thermally sprayed coating fractures may complement classical fractographic analysis to study specific failure mechanisms. In this paper, fracture of free-standing plasma sprayed ceramic (alumina) and metallic (stainless steel 316L)coatings during 3-point bending (3PB) was observed in-situ using a scanning electron microscope (SEM) in order to identify the most important failure mechanisms. Observations were supplemented by fractographic analysis of fractured specimens.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Surface and Coatings Technology
ISSN
0257-8972
e-ISSN
—
Volume of the periodical
205
Issue of the periodical within the volume
7
Country of publishing house
CH - SWITZERLAND
Number of pages
5
Pages from-to
—
UT code for WoS article
000286343100002
EID of the result in the Scopus database
—