Mechanical properties of plasma sprayed layers of NiAl10 and NiAl40 on AZ91 alloy

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F17%3A00489878" target="_blank" >RIV/61389021:_____/17:00489878 - isvavai.cz</a>

  • Result on the web

  • DOI - Digital Object Identifier

Alternative languages

  • Result language

    angličtina

  • Original language name

    Mechanical properties of plasma sprayed layers of NiAl10 and NiAl40 on AZ91 alloy

  • Original language description

    In this work, plasma coatings of NiAl10 and NiAl40 on magnesium alloy AZ91 substrate were prepared by the hybrid plasma spraying system WSP®-H 500. The both plasma sprayed coatings of NiAl10 and NiAl40 have metallurgical bond. The thicknesses of microstructures in the cross-section of NiAl10 and NiAl40 plasma sprayed coatings prepared by 9 passes were 374 and 440 μm respectively. Adhesion test of plasma sprayed layers was performed using a modified ASTM C 633 standard. The tensile adhesion strength values are 24.7 MPa for NiAl10 coatings and 12.3 MPa for NiAl40 coatings. Abrasion resistance according to Slurry Abrasion Response (SAR) test of NiAl40 layers had similar values (0.12 g/cm2)in a comparison with the uncoated AZ91 (0.126 g/cm2). Layers NiAl10 had greater weight losses (0.175 g/cm2) than uncoated AZ91. Microhardness of plasma coating of NiAl40 is several times greater than microhardnesses of plasma coating of NiAl10 and uncoated substrate AZ91

  • Czech name

  • Czech description

Classification

  • Type

    D - Article in proceedings

  • CEP classification

  • OECD FORD branch

    20501 - Materials engineering

Result continuities

  • Project

    <a href="/en/project/GP14-31538P" target="_blank" >GP14-31538P: Evolution of bonding interface during and after plasma spraying of metallic materials on magnesium and magnesium alloy</a><br>

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2017

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Article name in the collection

    METAL 2017 - 26th International Conference on Metallurgy and Materials, Conference Proceedings

  • ISBN

    978-80-87294-79-6

  • ISSN

  • e-ISSN

  • Number of pages

    6

  • Pages from-to

    1658-1663

  • Publisher name

    TANGER Ltd

  • Place of publication

    Ostrava

  • Event location

    Brno

  • Event date

    May 24, 2017

  • Type of event by nationality

    WRD - Celosvětová akce

  • UT code for WoS article

    000434346900267