Mechanical properties of Ti-15Mo alloy prepared by cryogenic milling and spark plasma sintering

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F19%3A00525648" target="_blank" >RIV/61389021:_____/19:00525648 - isvavai.cz</a>

  • Alternative codes found

    RIV/00216208:11320/19:10405716

  • Result on the web

    <a href="https://www.mdpi.com/2075-4701/9/12/1280" target="_blank" >https://www.mdpi.com/2075-4701/9/12/1280</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.3390/met9121280" target="_blank" >10.3390/met9121280</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Mechanical properties of Ti-15Mo alloy prepared by cryogenic milling and spark plasma sintering

  • Original language description

    Metastable β-Ti alloy Ti-15Mo was prepared by cryogenic ball milling in a slurry of liquid argon. Material remained ductile even at low temperatures, which suppressed particle refinement, but promoted intensive plastic deformation of individual powder particles. Repetitive deformation of powder particles is similar to the multidirectional rolling and resembles bulk severe plastic deformation (SPD) methods. Initial and milled powders were compacted by spark plasma sintering. Sintered milled powder exhibited a refined microstructure with small β-grains and submicrometer sized a-phase precipitates. The microhardness and the yield tensile strength of the milled powder after sintering at 850 °C attained 350 HV and 1200 MPa, respectively. Low ductility of the material can be attributed to high oxygen content originating from the cryogenic milling. This pioneering work shows that cryogenic milling followed by spark plasma sintering is able to produce two-phase β-Ti alloys with refined microstructure and very high strength levels.

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database

  • CEP classification

  • OECD FORD branch

    20501 - Materials engineering

Result continuities

  • Project

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2019

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    Metals

  • ISSN

    2075-4701

  • e-ISSN

  • Volume of the periodical

    9

  • Issue of the periodical within the volume

    12

  • Country of publishing house

    CH - SWITZERLAND

  • Number of pages

    14

  • Pages from-to

    1280

  • UT code for WoS article

    000506637800041

  • EID of the result in the Scopus database

    2-s2.0-85076117799