Aspect of Chip Formation during Turning of Hardened Steel 100Cr6
Original language description
The paper deals with analysis of chip formation and related aspects of the chip formation as chip thickness, chip ratio, shear angle and chip segmentation during turning hardened steel 100Cr6. The paper draws a comparison of some aspects of the chip formation between turning roll bearing steel in the annealed and turning roll bearing steel in the hardened state. The results of the analysis show that there is the formation of a segmented chip in the case of hard turning.
Czech name
Aspekty tvarování třísky během soustružení kalené oceli 100Cr6
Czech description
Článek se zabývá analýzou tvarování třísky a souvisejícími aspekty tvarování třísky jako je tloušťka, koeficient tloušťky třísky, úhel střihu a členění třísky během soustruženi kalené oceli 100Cr6. Článek vykresluje porovnání některých aspoektů tvarovánítřísky mezi soustružením ložiskové oceli v žáhaném a soustružením ložiskové oceli v kaleném stavu. Výsledky anylaýzy ukazují že segmentiová (článkovitá) tříska vzniká při tvrdém soustružení.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JR - Other machinery industry
OECD FORD branch
—

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)