Ultrafine grain formation during equal channel angular extrusion in an Al-Mg-Si alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F05%3A00012934" target="_blank" >RIV/61989100:27360/05:00012934 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Ultrafine grain formation during equal channel angular extrusion in an Al-Mg-Si alloy
Original language description
Microstructural development of aluminium alloy 6082 during equal-channel angular pressing was investigated to understand the mechanisms of grain refinement and strain accommodation. The samples were extruded at room temperature. Cross-section of originalsamples was 8 x 8 mm and their length was 32 mm. Deformation forces were measured during extrusion, resistance to deformation was calculated and deformation speed was determined approximately. Analysis of structure was made with use of light microscopyand SEM. Mechanical properties of samples after extrusion were determined by tensile test and by so called penetration test
Czech name
Ultra jemné tvářené zrna během ECAP v Al-Mg-Si slitině
Czech description
Vývoj mikrostruktury Al slitiny 6082 během ECAP byl zkoumán,aby bylo porozuměno mechanismu zjemnění zrn a napěťového vybavení. Vzorky byly protlačovány při pokojové teplotě. Průřez vzorků byl 8 x8 mm a jejich délka byla 32mm. Během protlačování byly měřeny deformační síly, odpor deformace byl počítán a deformační rychlost byla zkoumána přibližně. Analýza struktutry byla provedena s použitím světelného mikroskopu a SEM. Mechanické vlastnosti vzorků po protlačování byly zkoumány tahovou zkouškou a tak zvaným penetračnín testem