Numerical Analysis of a Transversal Crack in a Steel Slab

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F06%3A00014233" target="_blank" >RIV/61989100:27360/06:00014233 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Numerical Analysis of a Transversal Crack in a Steel Slab
Original language description
The paper deals with surface morphology, the mechanism of origination and causes of cross cracking of a concast low alloy manganese steel slab. It has been found that the cross cracking is characterized by high macroheterogeneity of manganese, carbon andsulphur. The causes of cross cracking were explained by means of a thermokinetic calculation of a slab transient temperature field and by means of an application of the original method of investigation into chemical heterogeneity of metallic alloys.
Czech name
Numerická analýza příčné trhliny v ocelové bramě
Czech description
Článek se zabývá morfologií povrchu, příčinami a mechanismem vzniku příčné trhliny v plynulé lité nízkolegované manganové ocelové bramě. Bylo zjištěno, že příčná trhlina je charakterizována vysokou makroheterogenitou manganu, uhlíku a síry. Příčiny vzniku příčné trhliny byly vysvětleny na základě termokinetických výpočtů teplotního pole bramy a pomocí aplikace původní metody výzkumu chemické heterogenity kovových slitin.

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)