Microstructure evolution of magnesium alloys

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00015933" target="_blank" >RIV/61989100:27360/07:00015933 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Microstructure evolution of magnesium alloys
Original language description
The paper presents characteristic physical-metallurigal properties of selected magnesium alloys at hot deformation. Special attention was devoted to analysis of deformation conditions on microstructure and final mechanical properties. Development of microstructure has been observed from as cast state till heat treatment T4. Deformation was made by rolling and hot torsion test on alloys AZ91, AZ61 and AZ31. After applies plastic deformation attention was paid also to share of individual types of deformation mechanisms.
Czech name
Vývoj mikrostruktury hořčíkových slitin
Czech description
V článku jsou uvedeny charakteristické fyzikálně-metalurgické vlastnosti vybraných hořčíkových slitin při deformaci za tepla. Pozornost je zaměřena na rozbor vlivu deformačních podmínek na mikrostrukturu a finální mechanické vlastnosti. Vývoj mikrostruktury je sledován od litého stavu až po tepelné zpracování T4. Deformace byla realizována válcováním a krutovou zkouškou za tepla na lsitinách AZ91, AZ61 a AZ31: Po provedené plastické deformaci byla věnována pozornost taktéž i na podíl jednotlivých typů deformačních mechanismů.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)