Influence of Cooling Rate on Microstructure of a NB-V HSLA steel.

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00016042" target="_blank" >RIV/61989100:27360/07:00016042 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Influence of Cooling Rate on Microstructure of a NB-V HSLA steel.
Original language description
In most cases an effort is made to combine controlled rolling of HSLA steel with its accelerated cooling, which has a favourable influence on mainly size of the resulting ferritic grain. In laboratory experiments mentioned below a simplified simulation of rolling of universal mill plates in a three-high mill was carried out, where slowed down cooling of final rolled products was used (given by temperature conditions in operation when rolled products are not water-sprayed and they cool from the finishingrolling temperature in collection pits).
Czech name
Vliv rychlosti ochlazování na mikrostrukturu NB-V HSLA oceli
Czech description
Zpomalené ochlazování HSLA oceli simuluje teplotní poměry ve sběrné jámě provozní válcovny trio, kde se postupně hromadí a pomalu chladnou hotové vývalky. Při těchto podmínkách dochází ke zhrubnutí a zvýšení heterogenity konečné mikrostruktury tvářenéhomateriálu, tím ke zhoršení mechanických vlastností, zejména křehkolomových. Takový materiál má naopak projít řízeně zrychleným ochlazením pro dosažení zjemněné struktury. To však v běžných provozních podmínkách válcoven není vždy umožněno.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)