The chemical composition and morphology of oxidic ceramics at filtration of steel deoxidised by aluminium

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F10%3A86076270" target="_blank" >RIV/61989100:27360/10:86076270 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
The chemical composition and morphology of oxidic ceramics at filtration of steel deoxidised by aluminium
Original language description
Composition and morphology of filter ceramics was investigated during filtration of steel deoxidised by aluminium. Filtration was realised with use of filters based on oxidic ceramics Cr2O3, TiO2, SiO2, ZrO2, Al2O3, 3Al2O3.2SiO2 and MgO.Al2O3. It was established that change of interphase (coating) occurs during filtration of steel on the surface of capillaries of ceramics, where content of basic oxidic component decreases. Loss of oxidic component in the coating is replaced by increase of oxides of manganese and iron and it is great extent inversely proportional to the value of Gibbs' energy of oxide, which forms this initial basis of ceramics.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)