DSC study of Fe?C?O based system
Original language description
The paper deals with the study of phase transformation temperatures of Fe (Fe?C?O) based metallic alloys. Three model alloys with graded carbon and oxygen content were used for experimental investigation. Low temperature region (below 1000 °C) was the investigated area. Phase transformation temperatures were obtained using DSC (Differential Scanning Calorimetry) and Netzsch STA 449 F3 Jupiter laboratory system. Under inert atmosphere (Ar 6N) DSC experiments of alloys were conducted. Controlled heating was conducted at the rate of 4 °C min-1. Region of eutectoid transformation (Fe?(C) + Fe3C _ Fe?(C)), alpha-gamma (Fe?(C) _ Fe?(C)) and transformation Fe?(O) + Fe0.92O _ Fe?(O) + Fe0.92O was studied. New original data (phase transformation temperatures) were obtained in this work. The relationship between shift of phase transformation temperatures and chemical composition (mainly carbon and oxygen content) is investigated in this paper. Comparison of the obtained experimental data with th
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)