Intensive plastic deformation of pre-sintered Al powder

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86095293" target="_blank" >RIV/61989100:27360/15:86095293 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Intensive plastic deformation of pre-sintered Al powder
Original language description
The influence of intensive plastic deformation on compacted Al powders was evaluated. The samples subjected to deformation processing were prepared from powder particles with diameters between 25 and 45 ?m, pre-compacted using double-step cold isostaticpressing (CIP) at 200+300 MPa applied for 30 seconds each and subsequently vacuum sintered at 500oC for 60 min. Analyses of chemical composition of the sintered samples were carried out using scanning electron microscopy, while microhardness measurementswere performed to evaluate the degree of compaction. The results showed increasing microhardness with increasing total imposed strain. Greater refinement of microstructure was achieved by increasing degrees of processing.
Czech name
—
Czech description
—

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
METAL 2015 : 24th International Conference on Metallurgy and Materials : full texts of papers : June 3rd-5th 2015, Hotel Voronez I, Brno, Czech Republic, EU
ISBN
978-80-87294-58-1
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
247-252
Publisher name
Tanger
Place of publication
Ostrava
Event location
Brno
Event date
Jun 3, 2015
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)