Effect of CaO/SiO2 ratio on viscosity and structure of slag

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F15%3A86095524" target="_blank" >RIV/61989100:27360/15:86095524 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Effect of CaO/SiO2 ratio on viscosity and structure of slag
Original language description
The objective of this work is experimental determination of temperature dependences of viscosity of the molten CaO Al2O3 SiO2 system and assessment of impact of CaO/SiO2 ratio on viscosity and structure of this system. Experimental measurements of viscosity were performed with use of the high-temperature viscometer Anton Paar FRS 1 600. Viscosity was measured in a rotational mode during heating at the rate of 3.3 oC/min in the temperature interval from 1 673 to 1 873 K. Viscosity in the molten oxide system is determined by the internal structure. Exact clarification of the change of structure of the oxide system caused by the increased content of CaO was performed by Fourier transform infrared spectroscopy.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/LO1203" target="_blank" >LO1203: Regional Materials Science and Technology Centre - Feasibility Program</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)