The influence of corrosion attack on grey cast iron brittle-fracture behaviour and its impact on the material life cycle
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F62156489%3A43210%2F17%3A43911790" target="_blank" >RIV/62156489:43210/17:43911790 - isvavai.cz</a>
Alternative codes found
RIV/62156489:43410/17:43911790
Result on the web
<a href="https://doi.org/10.11118/actaun201765041295" target="_blank" >https://doi.org/10.11118/actaun201765041295</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.11118/actaun201765041295" target="_blank" >10.11118/actaun201765041295</a>
Alternative languages
Result language
angličtina
Original language name
The influence of corrosion attack on grey cast iron brittle-fracture behaviour and its impact on the material life cycle
Original language description
The paper is concerned with brittle-fracture behaviour of grey cast iron attacked by corrosion and its impact on the life cycle of a spare part made of grey cast iron. In a corrosion chamber, outdoor climatic conditions (temperature and relative air humidity) were simulated in which degradation processes, induced by material corrosion, degrading mechanical properties of a material and possibly leading to irreversible damage of a machine component, occur in the material of maintenance vehicles that are out of operation for the period of one year. The corrosion degradation of grey cast iron, which the spare parts constituting functional parts of an engine are made of grey cast iron, is described with regard to brittle-fracture behaviour of the material. For the description of corrosion impact on grey cast iron, an instrumented impact test was employed. A corrosion degradation effect on grey cast iron was identified based on measured values of total energy, macro plastic deformation limit, initiation force of unstable crack propagation and force exerted on unstable crack arrest. In the first part of the experiment, a corrosion test of the material concerned was simulated in a condensation chamber; in the second part of the experiment, research results are provided for the measured quantities describing the material brittle-fracture behaviour; this part is supplemented with a table of results and figures showing the changes in the values of the measured quantities in relation to test temperatures. In the discussion part, the influence of corrosion on the values of unstable crack initiation and arrest forces is interpreted. In the conclusion, an overview of the most significant research findings concerning the impact of corrosion on the life cycle of grey cast iron material is provided.
Czech name
—
Czech description
—
Classification
Type
J<sub>SC</sub> - Article in a specialist periodical, which is included in the SCOPUS database
CEP classification
—
OECD FORD branch
20306 - Audio engineering, reliability analysis
Result continuities
Project
—
Continuities
S - Specificky vyzkum na vysokych skolach
Others
Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Acta Universitatis Agriculturae et Silviculturae Mendelianae Brunensis
ISSN
1211-8516
e-ISSN
—
Volume of the periodical
65
Issue of the periodical within the volume
4
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
7
Pages from-to
1295-1301
UT code for WoS article
—
EID of the result in the Scopus database
2-s2.0-85028852868