Preparation and Characterization of the Thin Nanocrystalline TiO2 Layers.

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F07%3A00091203" target="_blank" >RIV/67985858:_____/07:00091203 - isvavai.cz</a>
Alternative codes found
RIV/44555601:13440/07:00003935
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Preparation and Characterization of the Thin Nanocrystalline TiO2 Layers.
Original language description
The surface morphology, roughness, structural and textural properties of thin nanolayers of Titania that is promising as catalytic agent for removing of organic impurities from waste water and air, photovoltaic cell and pigment were studied. Gel nanolayers were prepared by repeated dip-coating of silica glass to transparent homogeneous sol. Transparent gel layers were converted to anatase layers by calcination at 400°C for 4 hours or by subcritic H2O extraction.
Czech name
Příprava a charakterizace tenkých nanokrystalických titaničitých vrstev.
Czech description
Byla studována povrchová morfologie, drsnost povrchu, strukturní a texturní vlastnosti tenkých titaničitých nanovrstev jakožto perspektivního materiálu pro aplikaci v oblasti katalýzy čistění odpadních vod a plynů, fotovoltaických článků a barviv. Gelovévrstvy byly připraveny opakovaným ponořováním křemičitého skla do připraveného solu. Kalcinací při 400°C po dobu 4 hodin nebo extrakcí podkritickou vodou byly transparentní gelové vrstvy přeměněny na krystalické anatasové vrstvy.

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)