Photocatalytic Decomposition of N2O on Ag-TiO2

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F67985858%3A_____%2F11%3A00364470" target="_blank" >RIV/67985858:_____/11:00364470 - isvavai.cz</a>
Alternative codes found
RIV/61989100:27730/11:86080626 RIV/61989100:27710/11:86080626
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Photocatalytic Decomposition of N2O on Ag-TiO2
Original language description
Catalysts with various Ag loading (0.7 ? 5.2 wt%) in the powder form were prepared by the sol-gel process controlled in the reverse micellar environment. X-ray diffraction (XRD), nitrogen adsorption measurement, UV-Vis and elemental analysis were employed for characterization of catalysts. Effect of various silver loadings on photocatalytic activity of TiO2 catalysts in N2O photocatalytic decomposition was studied. Photocatalytic decomposition of N2O was performed in annular batch reactor illuminated with 8 W Hg lamp (254 nm wavelength). Reaction kinetic corresponds to first-order reaction rate which is in agreement with plausible reaction mechanisms. The highest N2O conversion of 77% after 24 hours was reach over TiO2 modified by 3.4 wt% Ag. The Ag metal clusters could provoke a decrease in the electron-hole recombination rate.
Czech name
—
Czech description
—

Project
<a href="/en/project/GD203%2F08%2FH032" target="_blank" >GD203/08/H032: Advanced catalytic processes and materials</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)