Creep Resistance and Microstructural Stability of TAF 650 Steel.

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F01%3A07013135" target="_blank" >RIV/68081723:_____/01:07013135 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Creep Resistance and Microstructural Stability of TAF 650 Steel.
Original language description
The quantification of the particles of M23C6 and Laves phase in TAF 650 steel by means of image analysis and thermodynamic calculation of the amount of equilibrium phases were performed. It is shown that the growth rate of Laves phase is substantially higher than that of M23C6 carbide. The total area occupied by Laves phase precipitates represents 52.1 % of all particles area after creep (5888h, 100 MPa, 650 C). The equilibrium amount of secondary phases calculated by THERMO-Calc is in good agreement with experimental results.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2001
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Creep & Fracture of Engineering Materials and Structures.
ISBN
—
ISSN
—
e-ISSN
—
Number of pages
8
Pages from-to
196-203
Publisher name
Vítkovice - Research and Development
Place of publication
Ostrava
Event location
Praha [CZ]
Event date
Apr 8, 2001
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—

Similar results(10)