Constraint Effects at Brittle Fracture Initiation in Cast Ferritic Steel.
Original language description
The fracture resistance of cast low carbon manganese ferritic steel intended for containers for spent nuclear fuel has been analysed combining several approaches. Based on data from three-point bend specimens with shallow and deep cracks the effect of crack tip constraint at brittle fracture initiation has been followed. Q-parameter was used for the constraint quantification. The crack length effect on the fracture toughness-temperature diagram has been analysed and peculiarities of fracture behaviour in the lower shelf region have been explained. The role of cleavage fracture stress in brittle fracture initiation under the influence of crack tip constraint has been analysed.
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2001
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
Advances in Fracture and Damage Mechanics II.
ISBN
2-940130-14-0
ISSN
—
e-ISSN
—
Number of pages
6
Pages from-to
245-250
Publisher name
Hoggar
Place of publication
Ženeva
Event location
Miláno [IT]
Event date
Sep 18, 2001
Type of event by nationality
CST - Celostátní akce
UT code for WoS article
—